If I have the fused Clapton setup that the tfv12 rba kit comes with can I assume they are 316l?

[TFV12 RBA-T Wicking Tutorial]

9 hours ago, Adversarious1 said:

It looks like you are using TCR mode of your gx350 (I'm assuming there is a TCR setting where you can dial in the specific setting for a specific type of wire) and that looks like the temp co-efficient for SS304 wire.  If you are using SS304, then yes, that setting is good.  If you aren't using SS304 then I can't recommend the proper setting. 

Your best bet would be to use the basic setting for whatever type of wire you are using (Ni for nickel, Ti for Titanium or SS for stainless steel).  If it's kanthal, don't try to use it in TC mode.

Yea it's ss. What exactly does the setting change? 

[TFV12 RBA-T Wicking Tutorial]

On my gx350 when I'm setting up temp control is 0.00105 good? Or should I change that?